Polycarbonate · Technical data sheet
Polycarbonate printed-part properties
Printed-specimen values. X-Y = along layers, Z = across. Printed specimens, annealed and dried at 80 °C for 12 h.
Mechanical
| Tensile strength (X-Y) | 55 ± 4 MPa | ISO 527 |
| Tensile strength (Z) | 34 ± 3 MPa | ISO 527 |
| Young’s modulus (X-Y) | 2,110 MPa | ISO 527 |
| Young’s modulus (Z) | 1,450 MPa | ISO 527 |
| Elongation at break (X-Y) | 3.8% | ISO 527 |
| Elongation at break (Z) | 2.1% | ISO 527 |
| Flexural strength (X-Y) | 108 MPa | ISO 178 |
| Flexural strength (Z) | 55 MPa | ISO 178 |
| Flexural modulus (X-Y) | 2,310 MPa | ISO 178 |
| Flexural modulus (Z) | 1,620 MPa | ISO 178 |
| Charpy impact, unnotched (X-Y) | 79.7 kJ/m² | ISO 179 |
| Charpy impact, notched (X-Y) | 7.5 kJ/m² | ISO 179 |
| Charpy impact (Z) | 9.0 kJ/m² | ISO 179 |
Thermal
| HDT @ 0.45 MPa | 112 °C | ISO 75 |
| HDT @ 1.8 MPa | 117 °C | ISO 75 |
| Glass transition (Tg) | 145 °C | DSC |
| Vicat softening | 119 °C | ISO 306 |
Physical
| Density | 1.20 g/cm³ | ISO 1183 |
Manufacturer printed-specimen values — not a certified CoA or design allowables. Unlisted properties are not published for this grade; nothing here is estimated or interpolated.