ABS · Technical data sheet
ABS printed-part properties
Printed-specimen values. X-Y = along layers, Z = across. Printed specimens, annealed and dried at 80 °C for 12 h.
Mechanical
| Tensile strength (X-Y) | 33 ± 3 MPa | ISO 527 |
| Tensile strength (Z) | 28 ± 2 MPa | ISO 527 |
| Young’s modulus (X-Y) | 2,200 MPa | ISO 527 |
| Young’s modulus (Z) | 1,960 MPa | ISO 527 |
| Elongation at break (X-Y) | 10.5% | ISO 527 |
| Elongation at break (Z) | 4.7% | ISO 527 |
| Flexural strength (X-Y) | 62 MPa | ISO 178 |
| Flexural strength (Z) | 39 MPa | ISO 178 |
| Flexural modulus (X-Y) | 1,880 MPa | ISO 178 |
| Flexural modulus (Z) | 1,590 MPa | ISO 178 |
| Charpy impact, unnotched (X-Y) | 39.3 kJ/m² | ISO 179 |
| Charpy impact, notched (X-Y) | 21.5 kJ/m² | ISO 179 |
| Charpy impact (Z) | 7.4 kJ/m² | ISO 179 |
Thermal
| HDT @ 0.45 MPa | 87 °C | ISO 75 |
| HDT @ 1.8 MPa | 84 °C | ISO 75 |
| Vicat softening | 94 °C | ISO 306 |
Physical
| Density | 1.05 g/cm³ | ISO 1183 |
Manufacturer printed-specimen values — not a certified CoA or design allowables. Unlisted properties are not published for this grade; nothing here is estimated or interpolated.