PETG · Technical data sheet
PETG printed-part properties
Printed-specimen values. X-Y = along layers, Z = across. Printed specimens, annealed and dried at 65 °C for 8 h.
Mechanical
| Tensile strength (X-Y) | 51 ± 1 MPa | ISO 527 |
| Tensile strength (Z) | 35 ± 6 MPa | ISO 527 |
| Young’s modulus (X-Y) | 2,780 MPa | ISO 527 |
| Young’s modulus (Z) | 2,550 MPa | ISO 527 |
| Elongation at break (X-Y) | 9.5% | ISO 527 |
| Elongation at break (Z) | 5.2% | ISO 527 |
| Flexural strength (X-Y) | 75 MPa | ISO 178 |
| Flexural strength (Z) | 56 MPa | ISO 178 |
| Flexural modulus (X-Y) | 1,950 MPa | ISO 178 |
| Flexural modulus (Z) | 1,740 MPa | ISO 178 |
| Charpy impact, unnotched (X-Y) | 31.5 kJ/m² | ISO 179 |
Thermal
| HDT @ 0.45 MPa | 71 °C | ISO 75 |
Manufacturer printed-specimen values — not a certified CoA or design allowables. Unlisted properties are not published for this grade; nothing here is estimated or interpolated.